东北大学冶金学院;
采用加热水解法，制备出摩尔分数为3%的氧化钇稳定氧化锆(3YSZ)粉体试样，而后对其依次进行1 000℃煅烧、球磨粉碎、添加0.3%(质量分数)纳米氧化铝的处理，利用SEM,XRD,BET和连续单轴压制等表征手段，分析了经过不同处理的3YSZ粉体试样微观形貌及密度-压强半对数曲线的变化，并探究了添加纳米氧化铝对3YSZ粉体试样的烧结活性，以及其陶瓷耐压强度、抗水热劣化性能的影响.结果表明：球磨处理能够有效消除煅烧后3YSZ粉体中的硬团聚体，与未球磨粉体相比，经球磨处理的3YSZ陶瓷耐压强度由434 MPa增至670 MPa;烧结助剂纳米氧化铝的添加使3YSZ粉体烧结致密化温度降至1 350℃,陶瓷耐压强度增至1 119 MPa,且经45 h低温劣化加速实验，3YSZ陶瓷仍未发生T→M的相变现象.
| 141 | 0 | 35 |
| 下载次数 | 被引频次 | 阅读次数 |
[1] 杨勇.氧化锆粉末先驱体脱水工艺对团聚程度的影响研究[J].长江大学学报(自科版),2014(8):13-16.(Yang Yong.Study on the influence of dehydration process of zirconia powder precursor on agglomeration degree[J].Journal of Yangtze University (Natural Science Edition) ,2014(8):13-16.)
[2] Kaliszewski M S,Heuer A H.Alcohol interaction with zirconia powders[J].Journal of the American Ceramic Society,1990,73(6):1504-1509.
[3] 罗人豪，刘凯旋，刘志，等.氧化锆陶瓷低温老化研究进展[J].硅酸盐通报，2023,42(2):694-707.(Luo Renhao,Liu Kaixuan,Liu Zhi,et al.Research progress on low-temperature degradation of zirconia ceramics[J].Bulletin of the Chinese Ceramic Society,2023,42(2):694-707.)
[4] 毛骏飙，陈楷.氧化钇稳定四方氧化锆陶瓷的性能老化研究[J].材料导报，1997,11(5):38-41.(Mao Junbiao,Chen Kai.A study of mechanical properties degradation in Y-TZP[J].Materials Reports,1997,11(5):38-41.)
[5] Matsui K,Yoshida H,Ikuhara Y.Nanocrystalline,ultra-degradation-resistant zirconia:its grain boundary nanostructure and nanochemistry[J].Scientific Reports,2014,4:4758.
[6] Seiichiro L,Yoshida H,Matsui K,et al.Microstructure and surface segregation of 3 mol% Y2O3-doped ZrO2 particles[J].Journal of the American Ceramic Society,2006,89(9):2952-2955.
[7] Saha B P,Kumar V,Joshi S V,et al.Investigation of compaction behavior of alumina nano powder[J].Powder Technology,2012,224:90-95.
[8] 陈杰，林晨光，胡学晟，等.超细WC粉末中团聚体的强度[J].粉末冶金工业，2008,18(5):25-29.(Chen Jie,Lin Chenguang,Hu Xuesheng,et al.Strength of aggregates in ultrafine wc powder[J].Powder Metallurgy Industry,2008,18(5):25-29.)
[9] 韩敏芳，彭苏萍，杨翠柏，等.氧化锆纳米粉体烧结性能研究[J].材料科学与工艺，2004,12(1):29-32.(Han Minfang,Peng Suping,Yang Cuibai,et al.Research of ZrO2 nano powders sintering properties[J].Materials Science and Technology,2004,12(1):29-32.)
[10] He Y J,Winnubst L,Burggraaf A J,et al.Grain-size dependence of sliding wear in tetragonal zirconia polycrystals[J].Journal of the American Ceramic Society,1996,79(12):3090-3096.
基本信息:
DOI：10.14186/j.cnki.1671-6620.2025.01.012
中图分类号:TQ174.1
引用信息:
[1]尹言强,刘涛,韩磊.球磨与纳米氧化铝添加对3YSZ粉体及其陶瓷性质的影响[J].材料与冶金学报,2025,24(01):82-88.DOI:10.14186/j.cnki.1671-6620.2025.01.012.
基金信息:
国家自然科学基金资助项目(51974072); 中央高校基本科研业务费专项资金资助项目(N2125028)